Polyester T80 Seiliedig Castio polywrethan Prepolymer

HJ-3875

HJ-3880

HJ-3885

HJ-3890

NCO cant Cynnwys

2.6±0.2

3.0±0.2

3.5±0.2

4.3±0.2

Dwysedd25 degree /(g/cm³)

1.23

1.23

1.23

1.23

Gludedd80 degree /mpa·s

1800-2200

1700-2100

1500-1800

1200-1600

Ymddangosiad am 25gradd

Gwyn solet

Cymysgu Tymhereddgradd

Prepolymer/Moca

85 gradd /115 gradd

85 gradd /115 gradd

85 gradd /115 gradd

80 gradd / 115 gradd

Amser Gel/ mun

8-10

4-7

4-7

2-4

Amser Fwlcaneiddio (h)

25-16

25-16

25-16

25-16

Priodweddau Corfforol

Caledwch (Traeth A)

75±2

80±2

85±2

90±2

Cryfder Tynnol (Mpa)

30-37

38-45

42-48

45-50

Modwlws 100 y cant (Mpa)

9-10

9-10

10-11

10-12

Modwlws 300 y cant (Mpa)

14-15

14-15

15-17

17-20

Elongation at Break ( cant )

650-720

630-700

610-680

600-660

Cryfder rhwyg (KN/m)

60-70

75-82

82-95

100-115

Cywasgu anffurfiannau parhaol y cant

6-8

8-10

6-10

8-10

Colli sgraffiniad DIN（mm³）

Llai na neu'n hafal i 55

Llai na neu'n hafal i 50

Llai na neu'n hafal i 48

Llai na neu'n hafal i 45

Y cant gwydnwch /25gradd

24-26

23-25

20-23

18-22

Cymhwysiad cynnyrch: Gwialen a bar, dalen a phlât, caster, rholio llusgo, sgrin ddosbarthu, cyplu, glanhawr pibell Olew, cylch selio, seiclon, sgrafell a chynhyrchion eraill.

Manylion gweithredu:

Ar ôl di-nwyo gwactod ar 80-85 gradd, mae'r prepolymer yn cael ei gymysgu â MOCA wedi'i doddi ar gyfer castio a vulcanization. Mae'n addas ar gyfer gweithrediad llaw a mecanyddol.

Storio:

Storio mewn lle oer a sych a'i ddefnyddio cyn gynted â phosibl ar ôl agor; Os na ellir ei ddefnyddio ar un adeg, rhaid ei selio â nitrogen; Mae angen defnyddio'r ail agoriad ar gyfer defoaming, a'r cyfnod storio gwreiddiol yw chwe mis.

pacio:

Drwm 20kg neu 200kgiron

HJ-3832

HJ-3842

HJ-3893

HJ-3895

NCO cant Cynnwys

3.2±0.2

4.2±0.2

4.7±0.2

5.0±0.2

Dwysedd25 degree /(g/cm³)

1.23

1.23

1.23

1.23

Gludedd80 degree /mpa·s

1600-1800

1500-1700

1000-1200

900-1100

Ymddangosiad am 25gradd

Gwyn solet

Cymysgu Tymhereddgradd

Prepolymer/Moca

85 gradd /115 gradd

80 gradd / 115 gradd

80 gradd / 115 gradd

75 gradd /115 gradd

Amser Gel/ mun

4-6

3-5

2-3

2-3

Amser Fwlcaneiddio (h)

25-16

25-16

25-16

25-16

Priodweddau Corfforol

Caledwch (Traeth A)

82±2

90±2

93±2

95±2

Cryfder Tynnol (Mpa)

38-43

40-45

45-49

45-50

Modwlws 100 y cant (Mpa)

10-11

10-12

8-10

8-10

Modwlws 300 y cant (Mpa)

14-15

15-16

16-18

16-18

Elongation at Break ( cant )

650-750

580-700

570-680

550-680

Cryfder rhwyg (KN/m)

80-90

85-95

110-130

115-135

Cywasgu anffurfiannau parhaol y cant

4-6

4-6

2-4

2-4

Colli sgraffiniad DIN（mm³）

Llai na neu'n hafal i 55

Llai na neu'n hafal i 50

Llai na neu'n hafal i 45

Llai na neu'n hafal i 45

Y cant gwydnwch /25gradd

22-25

20-23

18-22

16-18

Cwmpas cymhwysiad cynnyrch: Gwialen a bar, Taflen a phlât, caster, rholio llusgo, sgrin ddosbarthu, cyplu, glanhawr pibell Olew, cylch selio, seiclon, sgrafell a chynhyrchion eraill.

Manylion gweithredu:

Ar ôl di-nwyo gwactod ar 80-85 gradd, mae'r prepolymer yn cael ei gymysgu â MOCA wedi'i doddi ar gyfer castio a vulcanization. Mae'n addas ar gyfer gweithrediad llaw a mecanyddol.

Storio:

Storio mewn lle oer a sych a'i ddefnyddio cyn gynted â phosibl ar ôl agor; Os na ellir ei ddefnyddio ar un adeg, rhaid ei selio â nitrogen; Mae angen defnyddio'r ail agoriad ar gyfer defoaming, a'r cyfnod storio gwreiddiol yw chwe mis.

pacio:

Drwm 20kg neu 200kgiron